Concrete Coatings

Concrete Coatings

-For prepared wet concrete substrates. -For use on concrete surface of offshore facilities.

Product details

725-H06-10 Wet-surface epoxy sealing coating-Light yellow

 

Product Description

 

-A transparent epoxy surface sealer with good penetration properties.

 

-It can tolerate wet surface.

 

-VOC less than 420g/L

 

Intended Uses

 

-For prepared wet concrete substrates.

 

-For use on concrete surface of offshore facilities.

 

 

 

 

Product Information

 

Volume Solids

95%±2%

 

Finish/Sheen

Matt

 

Typical Film Thickness

50microns dry (52microns wet)

Theoretical Coverage

1.9m2/L at typical film thickness

Mix Ratio

2.6:1(volume)2.8:1(weight)

Method of Application

 

Airless Spray

Recommended

 

Tip size range

0.38-0.53mm

 

 

Output pressure

≥15MPa

Air Spray

Tip size range

2.0-3.0mm

 

Output pressure

≥0.4MPa

Brush/Roller

For small area only

 

Thinner

Not recommended. Use only in exceptional circumstances (volume 5%)

Cleaner

HX-501

Induction Period

Not necessary

Drying Information

 

15℃

25℃

35℃

 

Touch Dry

2h

1.5h

45min

 

Hard Dry

24h

16h

12h

 

Pot Life

1.5h

1h

30min

 

Overcoating Data         Substrate Temperature

Overcoated by   

15℃

25℃

35℃

 

Min Max

Min Max

Min Max

 

725-H45-ZF101

20h 10d

16h 7d

12h 5d

 

725-H45-ZF101G

20h 10d

16h 7d

12h 5d

 

725-H53-38

20h 10d

16h 7d

12h 5d

 

Storage

Store in cool and dry conditions. Well ventilate. Keep away from hot and fire. Shelf Life: 12 months minimum at 25℃. Subject to re-inspection thereafter.

Pack Size

Part A

15.1kg/14.5L in 20 L container

 

Part B

5.3kg/5.5L in 6L container

Flash Point

Part A

Greater than 31℃

 

Part B

Greater than 31℃

 

Mixed paint

Greater than 31℃

 

 

Surface Preparation

 

All surfaces to be coated should be clean, dryand free from contamination.

 

Concrete surface

 

Pre-clean all surfaces by brooming and if necessary accomplished by scrubbing with heavy duty cleaner / degreaser or low pressure water cleaning or chemical washing to remove oils, grease, wax, fatty acids and other contaminations.

 

Removal of surface laitance, curing compound and creation of surface profile can be accomplished by grinding with a selection of hand tools or electrical equipment.

 

 

 

 

Limitations

This product will not cure adequately below 5℃. For maximum performance ambient curing temperature should be above 10℃

 

Apply in good weather when the humidity is lower than 85%.The concrete surface must be wiped without visible water.

Before overcoating 725-H06-10, it must be clean and dry.

The dry time and overcoating interval may change according to the environment factors.

Avoiding absorb the solvent steam and paint steam for long time. Skin and eyes must avoid contacting the paint. Pay attention to ventilate and fireproof when applying.

 

 

Duty statement

The data in the sheet base on the information from the laboratory and practice. The application may exceed the control, so we only ensure our product quality. We own the right of the data sheet modification without informing.

 

Hot Tags: concrete coatings, China, suppliers, manufacturers, factory, Asia, Africa, made in China
Feedback

Our Service

The company has been developed a series of ship coating products have been passed approval by CCS, LR, and DNV. The coatings systems hold independent intellectual property rights meet the requirements of corrosion on steel and concrete structures in harbors, wharfs, bridges, power stations, petrol-chemicals and civil engineering.

Feedback

Contact Us

Address:Room 214 2F No.149-2 Huangpu AVE Middle, TianHe District, Guangzhou City, China

Tel: +86-20-38993165

Fax: 86-20-38993165

E-mail: sales@huisinschem.com

CopyRight© Huisins New Material Technology Co.,Limited

Huisins New Material Technology Co.,Limited