Intermediate Paint

Intermediate Paint

-For use at offshore facility, chemical plant, and wind power tower, etc. -For use in atmospheric environment protection

Product details

725-H53-87 High Build Epoxy Intermediate Coating-Grey/White

 

Product Description

 

 

-A two pack high build epoxy coating.

 

-Suitable for application at low temperature.

 

-VOC less than 200g/L

 

Intended Uses

 

-For use in atmospheric environment protection

 

-For use at offshore facility, chemical plant, and wind power tower, etc.

 

 

 

Product Information

Volume Solids

80%±2%

Finish/Sheen

Gloss

Typical Film Thickness

200 microns dry (250microns wet)

Theoretical Coverage

4m2/L at typical film thickness

Mix Ratio

2:1volume3.4:1(mass)

Method of Application

 

Airless Spray

Recommended

 

Tip size range

0.38-0.53mm

 

 

Output pressure

≥17MPa

Air Spray

Tip size range

2.0-3.0mm

 

Output pressure

≥0.4MPa

Brush/Roller

For small area only

 

Thinner

Not recommended. Use only in exceptional circumstances (volume 5%)

Cleaner

HX-501

Drying Information

 

-5℃

10℃

25℃

35℃

Touch Dry

6h

2h

1h

0.5h

Hard Dry

48h

24h

18h

12h

Pot Life

6h

4h

3h

2h

 

 

Overcoating Data           Substrate Temperature

Overcoated by

-5℃

10℃

25℃

35℃

Min Max

Min Max

Min Max

Min Max

725-J43-5

48h

24h

18h

12h

725-BS43-91

48h

24h

18h

12h

725-H42-30

48h

24h

18h

12h

Storage

Store in cool and dry conditions. Well ventilate. Keep away from hot and fire. Shelf Life: 12 months minimum at 25℃. Subject to re-inspection thereafter

Pack Size

Part A

22kg/13.5L in 20L container

 

Part B

6.5kg/6.5L in 9.25 L container

Flash Point

Part A

Greater than 31℃

 

Part B

Greater than 28℃

 

Mixed paint

Greater than 31℃

 

 

 

 

Surface Preparation

 

All surfaces to be coated should be clean, dry and free from contamination.

 

Primed Surfaces

 

The primer surface should be dry free from all contamination and 725-H53-87 must be applied within the overcoating intervals specified (consult the relevant product data sheet).

 

Areas of breakdown, damage etc., should be prepared to the specified standard (e.gSa2½GB/T 8923.1-2011or Abrasive Blasting, or Power Tool Cleaning) and patch primed prior to the application of 725-H53-87.

 

    Metallic Zinc Primed Surfaces

 

Ensure that surface of the primer is clean, dry and free from contamination and zinc salts before application of 725-H53-87. Ensure zinc primers are fully cured before overcoating.

 

 

 

 

Limitations

 

This product will not cure adequately below -10℃. For maximum performance ambient curing temperature should be above -5℃

 

In common with all epoxy base coatings, 725-H53-87 will exhibit chalking of the firm on UV exposure.

 

Apply in good weather. Temperature of the surface to be coated must be least 3℃ above the dew point when the humidity is lower than 85%.

 

The dry time and overcoating interval may change according to the environment factors.

 

Avoiding absorb the solvent steam and paint steam for long time. Skin and eyes must avoid contacting the paint. Pay attention to ventilate and fireproof when applying.

 

Duty statement

The data in the sheet base on the information from the laboratory and practice. The application may exceed the control, so we only ensure our product quality. We own the right of the data sheet modification without informing.




 

Hot Tags: intermediate paint, China, suppliers, manufacturers, factory, Asia, Africa, made in China
Feedback

Our Service

The company has been developed a series of ship coating products have been passed approval by CCS, LR, and DNV. The coatings systems hold independent intellectual property rights meet the requirements of corrosion on steel and concrete structures in harbors, wharfs, bridges, power stations, petrol-chemicals and civil engineering.

Feedback

Contact Us

Address:Room 214 2F No.149-2 Huangpu AVE Middle, TianHe District, Guangzhou City, China

Tel: +86-20-38993165

Fax: 86-20-38993165

E-mail: sales@huisinschem.com

CopyRight© Huisins New Material Technology Co.,Limited

Huisins New Material Technology Co.,Limited