Offshore Port Industry Heavy Duty Spray Paint Anti Corrosive Coating Grey Red Marine Grade Paint

Detailed Product Description Heavy-duty Anti-corrosive Coating Grey/Red (725-H45-ZF101G) Product Description • A two pack epoxy heavy-duty anti-corrosive coating and it is characterized by good adhesion and excellent • VOC less than 180g/L Intended Uses • For use in heavy-duty anti-corrosive...

Product details

Detailed Product Description

Main Raw Material:EpoxyStandard Film Thickness:500 Microns Dry ( 640 Microns Wet)
Application Method:SprayColor:Grey/Red
Type:PrimerLuster:Half Glazed
Theoretical Spreading Rate:200Solids (vol %):≥55


Heavy-duty Anti-corrosive Coating Grey/Red (725-H45-ZF101G)
Product Description

• A two pack epoxy heavy-duty anti-corrosive coating and it is characterized by good adhesion and excellent
• VOC less than 180g/L

Intended Uses
• For use in heavy-duty anti-corrosive areas.
• For steel or tidal range zone of concrete stakes heavy-duty anti-corrosion .
• For interior circulatory water piles of power plant special strengthening anti-corrosion.
• Fror Interior wall of steel pipes and concrete of sewage treatment works ,power plants and chemical plants etc. Heavy-duty anticorrosion

Product Information
• Volume Solids 80%±3%
• Finish/Sheen Semi-Gloss
• Typical Film Thickness 500 microns dry ( 640 microns wet)
• Theoretical Coverage: 1.6㎡/lat typical film thickness
• Mix Ratio:3.4:1(Volume) 7:1(mass)
• Method of Application
   Airless Spray Tip size range 0.45-0.68mm
   Output pressure ≥17mpa
   Brush/Roller For small area only
• Thinner: Not recommended. Use water only in exceptional circumstances(Max5% by volume)
• Drying Information
   -5°C  5°C  25°C  35°C
   Touch Dry 4H 2H 1H 45min
   Hard Dry 48H 36H  20H 10H
   Pot Life 6H 4H 2H
   Overcoatings Data: Substrate Temperature
   Overcoated By
   -5°C 5°C 25°C 35°C
   Min Max Min Max Min Max Min Max
   48H 14d 36H 10d 24H 7d 10H 5d
• Storage: Store in cool and dry conditions, Well ventilate. Keep away from hot and fire.
   Shelf Life: 12Months minimum at 25°C.Subject to re-inspection thereafter.
• Pack Size:
   Park A 30KG/15.5L in 20L container
   Park B 4.3KG/4.5L in 6L container.
• Flash Point:
   Park A greater than 31°C
   Park B greater than 29°C
   Mixed paint greater than 31°C

Surface Preparation:
1. High pressure fresh water wash
or fresh water wash, as appropriate, and remove all oil or grease, soluble contaminants and other foreign matter in accordance with SSPC-SP1 solvent cleaning. All surfaces to be coated should be clean, dry and free from contamination.
2. Steel
Remove weld spatter and smooth weld seams and sharp edges. The surfaces should be blast cleaned to Sa2.5(GB/T8923-1988). The weld seams areas could be to St3(GB/T8923-1988) using power tool
Apply 725-H45-ZF101G before oxidation occurs. If oxidation has occurred, The entire oxidized area should be reblasted to the standard specified above.
3. Concrete
Remove loose powder of the cement, attached organisms,mud,oil or grease and other foreign matter thoroughly.
The surface can be abrade by blasing or using power tool to remove loose powder,attached organisms, mud etc. and oil can be cleaned by scour.

Repair/On Board Maintenance
A, Steel

The areas to be required should be cleaned to St3(GB/T 8923-1988) by mechanical method or higher level of surface prepared to Sa2.5 by abrasive blasting. Abrade the area immediately surrounding the repair to provide a key for subsequent coating application.Overlap areas should be kept to minimum.
B, Concrete
The areas to be required should be cleaned to St3(GB/T 8923-1988) by mechanical method or higher level of surface prepared to Sa2.5 by abrasive blasting. Abrade the area immediately surrounding the repair to provide a key for subsequent coating application.Overlap areas should be kept to minimum.

Limitations
• Apply in good weather. Temperature of the surface to be coated must be least 3°C above the dew point when the is lower than 85%
• In common with all epoxy base coatings, this product will exhibit chalking of the film on UV exposure.
• The dry time and over coating interval may change according to the environment factors.
• Avoiding absorb the solvent steam and paint steam for long time. Skin and eyes must avoid contacting the paint. Pay attention to ventilate and fireproof when applying.

33-1.jpg


Related Products
Feedback

Our Service

The company has been developed a series of ship coating products have been passed approval by CCS, LR, and DNV. The coatings systems hold independent intellectual property rights meet the requirements of corrosion on steel and concrete structures in harbors, wharfs, bridges, power stations, petrol-chemicals and civil engineering.

Feedback

Contact Us

Address:Room 214 2F No.149-2 Huangpu AVE Middle, TianHe District, Guangzhou City, China

Tel: +86-20-38993165

Fax: 86-20-38993165

E-mail: sales@huisinschem.com

CopyRight© Huisins New Material Technology Co.,Limited

Huisins New Material Technology Co.,Limited