Epoxy Sealing Coating

Epoxy Sealing Coating

Wet-surface epoxy sealing coating-Light yellow

Chat Now
Product details

Product Description:

--Model:725-H06-10

--A transparent epoxy surface sealer with good penetration properties.

--It can tolerate wet surface.

--VOC less than 200g/L.

Intended Uses:

--For prepared wet concrete substrates.

--For use on concrete surface of offshore facilities.

Product Information:

Volume   Solids:95%±2%                  Finish/Sheen  Matt

Typical Film Thickness

50microns dry (52microns wet)

Theoretical   Coverage(m2/L)

1.9m2/L at typical   film thickness

Mix Ratio: 2.6:1(volume)2.8:1(weight)

Method of   Application


Airless   Spray

Recommended

Tip size   range:0.38-0.53mm

Output   pressure:≥15MPa

Air Spray

 

Tip size   range:2.0-3.0mm

Output   pressure:≥0.4MPa

Brush/Roller

For small   area only

Thinner

Not   recommended. Use only in exceptional circumstances (volume 5%).

Cleaner

HX-501

Induction   Period

Not   necessary

Drying Information:


15

25

35

Touch Dry

2h

1.5h

45min

Hard Dry

24h

16h

12h

Pot Life

1.5h

1h

30min

Overcoating Data:


15

25

35

Overcoated by

Min Max

Min Max

Min Max

725-H45-ZF101

20h 10d

16h 7d

12h 5d

725-H45-ZF101G

20h 10d

16h 7d

12h 5d

725-H53-38

20h 10d

16h 7d

12h 5d

Storage:

Store in cool and dry conditions,Well ventilate.Keep away from hot and fire. Shelf Life: 12 months

minimum at 25℃,Subject to re-inspection thereafter.

 Pack Size:

Part A: 15.1kg/20L in 20L container

Part B: 5.3kg/5.5L in 6L container

 Flash Point:

Part A: Greater than 31℃

Part B: Greater than 31℃

Mixed pant: Greater than 31℃

Surface Preparation:

All surfaces to be coated should be clean, dry and free from contamination.

★Concrete surface

1)Pre-clean all surfaces by brooming and if necessary accomplished by scrubbing with heavy duty cleaner / degreaser or low pressure water cleaning or chemical washing to remove oils, grease, wax, fatty acids and other contaminations.

2)Removal of surface laitance, curing compound and creation of surface profile can be accomplished by grinding with a selection of hand tools or electrical equipment.

3)Weld seams and damaged areas should be blast cleaned to Sa2½(GB/T8923.1-2011).

★Shop Primed Steelwork.

If the shop primer shows extensive or wildly scattered breakdown overall sweepblasting may be necessary.

Limitations:

1)Apply in good weather. Temperature of the surface to be coated must be least 3℃ above the dew point when the is lower than 85%.

2)In common with all epoxy base coatings, 725-FH61-3 will exhibit chalking of the firm on UV exposure.

3)The dry time and overcoating interval may change according to the environment factors.

4)Avoiding absorb the solvent steam and paint steam for long time. Skin and eyes must avoid contacting the paint. Pay attention to ventilate and fireproof when applying.

Duty statement:

●The data in the sheet base on the information from the laboratory and practice.

●The application may exceed the control, so we only ensure our product quality.

●We own the right of the data sheet modification without informing.

   

Hot Tags: epoxy sealing coating, China, suppliers, manufacturers, factory, Asia, Africa, made in China
Related Products
Feedback

Our Service

The company has been developed a series of ship coating products have been passed approval by CCS, LR, and DNV. The coatings systems hold independent intellectual property rights meet the requirements of corrosion on steel and concrete structures in harbors, wharfs, bridges, power stations, petrol-chemicals and civil engineering.

Feedback

Contact Us

Address:Room 603 6F No 140 Huagang Business Building Zhongshan AVE West, TianHe District, Guangzhou City, China

Tel: +86-20-38993165

Fax: 86-20-38993165

E-mail: sales@huisinschem.com

CopyRight© Huisins New Material Technology Co.,Limited