Aluminiferous and Bituminous Anticorrosive Marine Fouling Release Coating Paint -Grey Colors

Technical Specification Product Name: Aluminiferous And Bituminous Anticorrosive Paint -Grey. Model No: 725-L44-01 Product Description 1. A quick one pack bituminous anticorrosive paint 2. VOC less than 350 g/L Intended Uses 1. Economic anticorrosive coatings for use in all under water areas. 2....

Product details

Technical Specification
Product Name: Aluminiferous And Bituminous Anticorrosive Paint -Grey.
Model No: 725-L44-01

Product Description
1. A quick one pack bituminous anticorrosive paint
2. VOC less than 350 g/L

Intended Uses
1. Economic anticorrosive coatings for use in all under water areas.
2. For use at Newbuilding, Maintenance and Repair or Maintenance

Product Information
1. Volume Solids 62%±3%
2. Finish/Sheen matt
3. Typical Film Thickness 75 microns dry ( 120 microns wet)
4. Theoretical Coverage: 8.3㎡/L at typical film thickness
5. Mix Ratio: one pack
6. Method of Application
    Airless Spray Tip size range 0.38-0.53mm
    Output Pressure ≥17MPa
    Air Spray Tip size range 2-3mm
    Output Pressure ≥0.4MPa
    Brush/Roller Need to coat several times to get film thickness
7. Thinner: Not recommended .Use water only in exceptional circumstances(max 5% by volume)
8. Drying Information 
    -5°C 5°C 25°C 35°C
    Touch Dry 2H 1H 30min 15min
    Hard Dry 48H 36H 24H 12H
    Pot Life Not applicable
    Overcoatings Data: Substrate Temperature
    Overcoated By 
    -5°C 5°C 25°C 35°C
    Min Max Min Max Min Max Min Max
    725-L44-02 48H no 36H no 24H no 24H no
    725-B40-6 48H no 36H no 24H no 24H no
9. Storage: Store in cool and dry conditions, Well ventilate. Keep away from hot and fire.Store temperature should be higher than 0°C.
    Shelf Life: 12Months minimum at 25°C。Subject to re-inspection thereafter.
10. Pack Size: 21.6kg/18L in 20L container
      Surface Preparation: The surface should be cleaned oil or grease, dust, and other foreign matter to keep clean and dry.

Surface Preparation:
1. High pressure fresh water wash or fresh water wash, as appropriate, and remove all oil or grease, soluble contaminants and other foreign matter in accordance with SSPC-SP1 solvent cleaning. All surfaces to be coated should be clean, dry and free from contamination.
2. Newbuilding
Remove weld spatter and smooth weld seams and sharp edges. The surfaces should be blast cleaned to Sa2.5(GB/T8923-1988). The weld seams areas could be to St3(GB/T8923-1988)
Apply 725-L44-01 before oxidation occurs. If oxidation has occurred, The entire oxidized area should be reblasted to the standard specified above.
3. Repair/On Board Maintenance
The areas to be required should be cleaned to St3(GB/T 8923-1988) by mechanical method or higher level of surface prepared to Sa2.5 by abrasive blasting. Abrade the area immediately surrounding the repair to provide a key for subsequent coating application. Overlap areas should be kept to minimum.

Limitations
a. Apply in good weather, Temperature of the surface to be coated must be least 3°C above the dew point when the humidity is lower than 85%
b. The dry time and over coating interval may change according to the environment factors.
c. Forbid to trample or pullute the surface of AF3-1 and coat the next paint before the film is hard dry.

16-1(001).jpg


Related Products
Feedback

Our Service

The company has been developed a series of ship coating products have been passed approval by CCS, LR, and DNV. The coatings systems hold independent intellectual property rights meet the requirements of corrosion on steel and concrete structures in harbors, wharfs, bridges, power stations, petrol-chemicals and civil engineering.

Feedback

Contact Us

Address:Room 214 2F No.149-2 Huangpu AVE Middle, TianHe District, Guangzhou City, China

Tel: +86-20-38993165

Fax: 86-20-38993165

E-mail: sales@huisinschem.com

CopyRight© Huisins New Material Technology Co.,Limited

Huisins New Material Technology Co.,Limited