Marine Shield Coating

Marine Shield Coating

Anodic shield coating-Yellow

Chat Now
Product details


Product Description:


-Model:725-8702-5 

-A two pack epoxy coating

-Quickly drying and applying

-VOC is 0g/L

 


Intended Uses

 

-Shielding coating for marine applied current cathodic protection system and protective coating for pipe joint.

 

-For hull and steel structure to fill holes caused by cavitation corrosion or pitting.


 

Product Information




Drying Information 




Overcoating Data




Storage:


Store in cool and dry conditions,Well ventilate.Keep away from hot and fire. Shelf Life: 12 months

minimum at 25℃,Subject to re-inspection thereafter.


 

Systems and Compatibility:

 

Consult your Sunrui Representative for the systems best suited for the surfaces to be protected.

 


Surface Preparation:

 

High pressure fresh water wash or fresh water wash, as appropriate, and remove all oil or grease, soluble contaminants and other foreign matter in accordance with SSPC-SP1 solvent cleaning. All surfaces to be coated should be clean, dry and free from contamination.

 

Newbuilding/Major Refurbishment:

 

725-AF3-1 can be applied over a recommended primer coating scheme. The primer surface should be clean, dry and free from contamination. 725-AF3-1 must be applied within the coating interval specified (consult the relevant product data sheet). Areas of breakdown, damage etc. should be prepared to the specified standard (eg.  St3) and primed prior to the application of 725-AF3-1.


The surface should be clean with solvent or water to remove oil or dust when 725-AF3-1 should be applied on cloth or wood substrate.

 


Repair


725-AF3-1 may be applied directly over aged 725-AF3-1 following thorough fresh water washing and degreasing provided the coating to be overcoated is in an intact and tightly adherent condition. Loose or flaking coatings should be removed back to a firm edge and 725-AF3-1 or an appropriate primer should be used to repair the area before application of the full coat.

 


Limitations:

 

725-AF3-1 should be applied over a recommended primer coating scheme. The primer surface should be clean, dry and free from contamination.

 

725-AF3-1 must be applied within the coating interval specified (consult the relevant product data sheet). Areas of breakdown, damage etc. should be prepared to the specified standard (eg. St3) and primed prior to the application of 725-BS43-91.

 

Apply in good weather. Temperature of the surface to be coated must be least 3℃above the dew point when the temperature is more than 0  and the humidity is lower than 85%.

 

It must be ventilate above 8h at pool ventilation area.

 

The dry time and overcoating interval may change according to the environment factors.

 

Forbid to trample or pollute the surface of 725-AF3-1 and coat the next paint before the film is hard dry.

 


Duty statement:

 

The data in the sheet base on the information from the laboratory and practice.

 

The application may exceed the control, so we only ensure our product quality.

 

We own the right of the data sheet modification without informing.



Hot Tags: marine shield coating, China, suppliers, manufacturers, factory, Asia, Africa, made in China
Related Products
Feedback

Our Service

The company has been developed a series of ship coating products have been passed approval by CCS, LR, and DNV. The coatings systems hold independent intellectual property rights meet the requirements of corrosion on steel and concrete structures in harbors, wharfs, bridges, power stations, petrol-chemicals and civil engineering.

Feedback

Contact Us

Address:Room 603 6F No 140 Huagang Business Building Zhongshan AVE West, TianHe District, Guangzhou City, China

Tel: +86-20-38993165

Fax: 86-20-38993165

E-mail: sales@huisinschem.com

CopyRight© Huisins New Material Technology Co.,Limited