General Epoxy Zinc Yellow Shop Primer Rust Protection Paint Marine Coating

Technical Specification Product Name: Epoxy Zinc yellow primer Model Name: 725-H06-19 Product Description 1. A two pack epoxy primer containing zinc yellow anticorrosive pigment 2. VOC is 300 g/L Intended Uses 1. For use at aluminum alloy 2. For use at Newbuilding, Maintenance and Repair or on...

Product details

Technical Specification
Product Name: Epoxy Zinc yellow primer
Model Name: 725-H06-19

Product Description
1. A two pack epoxy primer containing zinc yellow anticorrosive pigment
2. VOC is 300 g/L

Intended Uses
1. For use at aluminum alloy
2. For use at Newbuilding, Maintenance and Repair or on board maintenance.

Product Information
1. Volume Solids 63%±3%
2. Finish/Sheen matte
3. Typical Film Thickness 100microns dry (159microns wet)
4. Theoretical Coverage: 6.3㎡/L at typical film thickness
5. Mix Ratio: 3:1(volume) 5:1(mass)
6. Method of Application
    Airless Spray Tip size range 0.38-0.53mm
    Output Pressure ≥17MPa
    Air Spray Tip size range 2-3mm
    Output Pressure ≥0.4MPa
    Brush/Roller Need to coat several times to get film thickness
7. Thinner: Not recommended .Use water only in exceptional circumstances(max 5% by volume)
8. Drying Information 
    10°C 25°C 35°C
    Touch Dry 6H 4H 2H
    Hard Dry 48H  24H 20H
    Pot Life 6H 4H 2H
    Overcoatings Data: Substrate Temperature
    Overcoated By 
    10°C 25°C 35°C
    725-H06-19 36H 14D 20H 7d 16H 5D
    725-H53-81 36H 14D 20H 7d 16H 5D
    725-BS43-91 48H no 36H no 24H no
    725-H42-30
9. Storage: Store in cool and dry conditions, Well ventilate. Keep away from hot and fire.Store temperature should be higher than 0°C.
    Shelf Life: 12Months minimum at 25°C, Subject to re-inspection thereafter.
10. Pack Size:
      Park A:23.5kg/16.5L in 20L container
      Park B:4.7kg/5L in 6L container

Surface Preparation:
1. High pressure fresh water wash or fresh water wash, as appropriate, and remove all oil or grease, soluble contaminants and other foreign matter in accordance with SSPC-SP1 solvent cleaning. All surfaces to be coated should be clean, dry and free from contamination.
2. Aluminum or light alloy
3. The surface should be solvent cleaned to keep clean,dry and free from metal corrosion products
4. The substrate should be cleaned gently by sand paper,and then coated primer
Repair/Maintenance
1.Aluminum or light alloy
2.The areas to be repaired should be cleaned to metal by mechanical method abrade the area immediately surrounding the repair to provide a key for subsequent coating application. Overlap areas should be kept to a minimum.

Limitations
a. This product will not cure adequately below 5°C。For maximum performance ambient curing temperature should be above 10°C
b. Apply in good weather, Temperature of the surface to be coated must be least 3°C above the dew point when the humidity is lower than 85%
c. In common with all epoxy base coatings. 725-H06-19 will exhibit chalking of the film on UV exposure.
d. The dry time and over coating interval may change according to the environment factors.
e. Forbid to trample or pullute the surface of AF3-1 and coat the next paint before the film is hard dry.


Related Products
Feedback

Our Service

The company has been developed a series of ship coating products have been passed approval by CCS, LR, and DNV. The coatings systems hold independent intellectual property rights meet the requirements of corrosion on steel and concrete structures in harbors, wharfs, bridges, power stations, petrol-chemicals and civil engineering.

Feedback

Contact Us

Address:Room 214 2F No.149-2 Huangpu AVE Middle, TianHe District, Guangzhou City, China

Tel: +86-20-38993165

Fax: 86-20-38993165

E-mail: sales@huisinschem.com

CopyRight© Huisins New Material Technology Co.,Limited

Huisins New Material Technology Co.,Limited